Preparation and Property Study of UV-absorbing Fluorine-silicon Acrylic Resin
Abstract
A kind of UV-absorbing fluorine-silicon acrylic resin was prepared by solution copolymerization with vinyltrimethoxysilane(VTMS),hexafluorobutyl methacrylate(HFMA) and 2-(4-Benzoyl-3-hydroxyphenoxy) ethyl acrylate(BHEA) as modifying monomers. The acrylic polymers were characterized by Fourier transform infrared spectrum(FT-IR),Ultraviolet(UV) absorption spectrum;and the coatings thereof were studied by thermogravimetric analysis(TGA),water contact angle(CA) and Xenon lamp artificial accelerated aging tests. The results showed that the resins contained modifying groups and exhibited high UV absorbing performance, and the coatings showed good heat-resistance and hydrophobicity with the water CA of 92°. Meanwhile, the weather-resistance was promoted under the enduring protection of the modifying monomers. After 1 000 h aging test,the color difference and gloss retention of coatings were 3.12 and 80.4%, respectively.
Keywords: acrylic resin, fluorine-silicone, UV-absorbing, thermal stability, hydrophobicity, weather-resistance
Full Text:
PDFReferences
HE D L, ZHANG R, LEI H B, et al. Mathematical model of anti–ag– ing induces for acrylic polyurethane Coating[J]. Journal of Hunan University(Natural Sciences), 2016, 43 (12):98—103. (In Chinese)
XU G L, DENG C Y, XING L,et al. Preparation and properties of siloxane–modified styrene–acrylate latex particles with sore–shell structure [J]. International Journal of Polymeric Materials and Polymeric Biomaterials, 2013,62:488—492.
BISWAL T, SAMAL R, SAHOO P K. Microwave–assisted preparation of poly (2–EHA–so–ST) copolymer and poly (2–EHA–so–ST) /MMT nanocomposite [J]. Journal of Applied Polymer Ssiense, 2015, 125:1467—1475.
MISHRA S, SINGH J, CHOUDHARY V. Synthesis and sharasterisation of butyl acrylate/methyl methacrylate/glycine methacrylate latexes [J]. Journal of Applied Polymer Science, 2010, 15:549— 557.
SHIN M S, LEE Y H, RAHMAN M M,et al. Synthesis and properties of waterborne fluorinated polyurethane –acrylate using a sol– vent–/emulsifier–free method[J]. Polymer, 2013, 54:4873—4882.
XIAO X Y, XU R. Preparation and surface properties of core–shell polyacrylate latex containing fluorine and silicon in the shell [J]. Journal of Applied Polymer Science, 2011, 119 :1576—1585.
WANG Y, LIU F G, XUE X X. Morphology and properties of UV– curing epoxy acrylate coatings modified with methacryl–POSS[J]. Progress of Organic Coatings, 2015, 78:404—410.
BAE Y Y, LIM D H, PARK J B, et al. Adhesion performance and surface characteristics of low surface energy PSAs fluorinated by UV polymerization [J]. Polymer Engineering and Science, 2013, 53:1968—1978.
YU Y, LIAO B, JIANG S L, et al. Synthesis and characterization of photosensitive –fluorosilison –urethane acrylate prepolymers [J]. Designed Monomers and Polymers, 2015, 18:199—209.
ZHAO F C, ZENG X R, LI H Q, et al. Preparation of fluorinated polyacrylate composite latex with in situ generated nano–silica dis– persion and film durability [J], Iranian Polymer Journal, 2013, 22: 588—784.
PAN C L, ZHANG H, HU Z H, et al. Preparation of multilayered core–shell styrene–asrylis ?uorine monomer modifed emulsion[J]. China Synthetic Resin and Plastics, 2015, 05:5—8. (In Chinese)
PARK H S, DIM S R, PARD H J, et al. Preparation and characterization of weather resistant silisone/acrylic resin coatings[J]. Journal of Coatings Technology, 2003, 75(936), 55—64.
Refbacks
- There are currently no refbacks.